TEM study was made to explore the mechanism of the strain-age hardening of initially-dis- ordered (Co_(78)Fe_(22))_3V,which was found to be attributed to the formation of a special disloca- tion-stacking fault configuration in company with disorder-order transformation-disloca- tions extended to stacking faults on{111}planes and got connected with each other through partial dislocation reaction at intersections of{111}planes,leading to dense networks with cells bounded by stacking fault tetrahedrons.The results also indicated that ordered (Co_(78)Fe_(22))_3V has very low stacking fault energy on{111}planes and relative high and isotropie antiphase boundary energy,which implies that it is most likely to be Lomer-Cottrell locks,not Kear-Wilsdof locks,that are responsible for the high strength at high temperatures of this alloy.
关键词:
(Co
,
null
,
null
,
null